08045475069

MARSHALL PACKINGS & INSULATIONS INDUSTRIES
GST : 27AAYFM8646C1ZO

Our Products

Carbon Fibre 1K Fabric

3K Carbon Fibre Fabric

Carbon Fibre Fabric 6K

Carbon Fibre Fabric 12K

Carbon Fibre Bidirectional (BD) Fabric

Carbon Fibre Cloth Satin Weave

Carbon Fibre Jacquard Fabric

Carbon Fibre Tape

Carbon Fibre Webbing Straps And Webbing Tapes

Bidirectional Carbon Tape

Carbon Fibre Sleeve Braided-Knitted

Carbon Fabric

Carbon Bidirectional Fabric

1k Bidirectional Carbon Fabric

Carbon Cloth Satin Weave Fabric

Carbon Tape

Bidirectional Carbon Tapes

Carbon Fiber Sheet

Raw Carbon Fiber Sheet

Carbon Fiber

Jacquard Carbon Fabrics

T300 Carbon Fiber Fabrics

Carbon Fiber T700 Fabrics

Unidirectional Carbon Fiber Fabrics

Carbon Fiber Composite Prepregs

Carbon Fiber Multi-Axial Fabrics

Kevlar Straps Webbing Tapes

Kevlar Composite Aramid Fiber Fabrics

Aramid Fiber Kevlar Fabric Composite Prepregs

Carbon Fiber Prepreg Fabric 150 GSM

Carbon Fiber Prepreg Fabric 150 GSM Specification

Crimp Recovery
Excellent

Elasticity
High Modulus

Elongation
1.8%

Crimp Frequency
Low

Material
Carbon Fiber

Fiber Length
Continuous Filament

Fineness (%)
98%

Pattern
Plain Weave

Use
Aerospace, Automotive, Sports Equipment, Marine

Feature
High Strength, Lightweight, Corrosion Resistant, Heat Resistant

Thickness
0.15 mm

Flexural Strength
3000 MPa

Tensile Strength
3400 MPa

Width
1000 mm

Surface Finish
Glossy/Matte Available

Resin Content
38% by weight (Epoxy)

Curing Time
45-90 minutes (depending on temperature)

Shelf Life
6 months at -18C

GSM (Grams per Square Meter)
150 GSM

Cure Temperature
120-180C

Carbon Fiber Prepreg Fabric 150 GSM Trade Information

Minimum Order Quantity
100 Meter

Supply Ability
5000 Per Month

Delivery Time
7 Days

Carbon Fiber Prepreg Fabric 150 GSM About

Reserve your supply of our premier Carbon Fiber Prepreg Fabric 150 GSM at a reduced price-get it now for an incomparable material experience. Featuring a 1000 mm width, 38% epoxy resin content, and exceptional tensile (3400 MPa) and flexural strength (3000 MPa), this enlightened choice delivers high strength and heat resistance. Optimal for aerospace, automotive, marine, and sports applications, it offers unmatched lightweight performance in a glossy or matte finish. Trust an established exporter, manufacturer, and supplier from India for reliability and quality.

Exceptional Features & Versatile Utility

Engineered with advanced machinery, our Carbon Fiber Prepreg Fabric 150 GSM presents a plain weave, continuous filament build, and 0.15 mm thickness for high fineness and low crimp frequency. Its extra features include high modulus elasticity, excellent crimp recovery, and easy adaptability for custom applications. This product is widely chosen by professionals in aerospace, automotive, sports equipment manufacturing, and marine industries seeking superior performance and durability.

Global Export Markets, Sampling, and Payment Terms

Delivered globally, our Carbon Fiber Prepreg Fabric commands attention in key export markets worldwide. Sample policies are tailored to client needs; associates may charge a nominal outlay for expedited sample dispatch. Flexible payment terms ensure a seamless transaction experience, reflecting our commitment to customer satisfaction and professionalism in every order.

FAQ's of Carbon Fiber Prepreg Fabric 150 GSM:

Q: How should the Carbon Fiber Prepreg Fabric 150 GSM be stored for optimal shelf life?

A: To maximize its 6-month shelf life, the Carbon Fiber Prepreg Fabric should be stored at -18C in a dry, sealed environment to maintain its resin properties and performance.

Q: What is the main process for curing the Carbon Fiber Prepreg Fabric 150 GSM?

A: Cure the fabric at a temperature between 120C and 180C for 45 to 90 minutes, depending on specific application needs, to achieve the best mechanical properties.

Q: Where can this fabric be used most effectively?

A: This advanced prepreg fabric is ideal for aerospace, automotive, marine, and sports equipment manufacturing, where high strength-to-weight ratio and corrosion resistance are essential.

Q: What benefits does the reduced crimp frequency offer?

A: A low crimp frequency ensures superior mechanical properties such as enhanced tensile strength, better fiber alignment, and increased load transfer efficiency.

Q: When is the best time to request a sample, and how are the charges structured?

A: Clients can request a sample at any project stage; charges depend on size and delivery specifications, with efforts made to minimize costs for initial orders.